Basic Info.
Model NO.
40x13x3mm
Customized
Non-Customized
Application
Metal Recycling Machine, Metal Cutting Machine, Metal Straightening Machinery, Metal Spinning Machinery, Metal Processing Machinery Parts, Metal forging Machinery, Metal Engraving Machinery, Metal Drawing Machinery, Metal Coating Machinery, Metal Casting Machinery
Hardness
89.8hra
Density
14.7g/cm3
T.R.S
2800MPa
Length
40mm
Width
13mm
Thickness
3mm
Transport Package
25kg. Carton
Specification
YG8
Trademark
ZZUP
Origin
Zhuzhou, Hunan, China
HS Code
820900100
Production Capacity
100000kg/Month
Packaging & Delivery
Package Size
18.00cm * 11.00cm * 13.00cm
Package Gross Weight
8.000kg
Product Description
Overpressure sintering tungsten carbide plates have excellent red toughness,high hardness,good wear resistance,high elasticmodulus,high strength,good chemical stability,acid,alkali,
high temperature oxidation,Low impact toughness,low expansion coefficient,thermal conductivity,the characteristics of the conductive similar to iron and other alloy.
1. having all kind sizes for your choose,can suply less than 400mm length.
2. Sintere by vacuum sintering furnace and HIP machine with excellent specifications without any hole.
3. suply blank plate with tolerance(-0.15~+0.15)or (0~+0.3).
4. can grinding and polishing the side and blading.
5. delivery time is 12 days.
Customization Support!
| Grade | YG8 |
| Length | 40mm |
| Width | 13mm |
| Thickness | 3mm |
| Density | 14.7g/cm3 |
| Hardness | 89.8hra |
| T.R.S | 2800MPa |
| grade | Density (g/cm³) | T.R.S(Mpa) | Hardness HRA | performance& application recommended | Equivalent to ISO |
| YG6 | 14.8 | 2150 | 90.0 | High wear resistance,used for processing hard wood,original wood,aluminum section bar,brass rod and cast iron. | K20 |
| YG6A | 14.9 | 1860 | 92.0 | Better wear resistant than YG6,used for processing hard wood,original wood,aluminum section bar,brass rod and cast iron. | K10 |
| YG8 | 14.8 | 2320 | 89.5 | Wear and perussion resistance,used for processing hard wood,soft wood,ferrous and non-ferrous | K30 |
| YS2T | 14.6 | 2350 | 92.0 | Fine grain carbide with high wear resistance,high bending strength ,high resistance to bonding and high thermal strenght.apply to machining refractory alloys/stainless steel and high manganness steel ect. | M10 |
| YS25 | 13.8 | 2200 | 91.0 | Carbide grade with high hardness and good wear-resistance,suitable for rough turning,milling and planing of carbide steel,cast steel,high intensity steel and steel alloy | P25 |
| YL10.2 | 14.5 | 2150 | 92.2 | Wear resistance and strength comparatively higher,suitable for processing castiron,non-ferrous,and non-metal materials | / |
| Length(mm) | Weight(mm) | Height(mm) | Remarks |
| 300 | 200 | 10-45 | 1.Advising HIP sintered for thr plate which the thickness pore than 10mm. 2.befor delivery to you,all plates were detected by no damage ultrasonice. keeping the plates all are no blister,no pore,high desity&strength,impact resistance and long working life. 3.we can supply rough grinding or grinding the board surfaces. |
| 200 | 200 | 10-45 | |
| 200 | 20 | 10-45 | |
| 150 | 150 | 10-45 | |
| 150 | 130 | 10-45 | |
| 150 | 100 | 10-45 | |
| 150 | 80 | 10-45 | |
| 120 | 120 | 10-45 | |
| 105 | 105 | 10-45 | |
| 100 | 100 | 10-45 | |
| 100 | 50 | 10-45 | |
| 100 | 45 | 10-45 | |
| 80 | 55 | 10-45 | |
| 80 | 40 | 10-45 | |
| 70 | 35 | 10-45 | |
| 45 | 25 | 10-45 | |
| 35 | 19 | 10-45 | |
| 20 | 20 | 10-45 | |
| 18 | 12 | 10-45 | |
| ... | ... | ... |
Pulverizing to formula→ according to the requirements of USES→ the wet and dry mix → crushing -→and sieving to join after forming agent→sieve made the mixture→drying granulating and repression→molding →low-pressure sintering →molding (blank) to flaw detection, →packing and warehousing